Synthesis and Characterization of Massive Molybdenum Carbides and Supported CarbideContaining Catalysts Mo2C/C Prepared through Mechanical Activation Научная публикация
| Журнал |
Catalysis in Industry
ISSN: 2070-0504 , E-ISSN: 2070-0555 |
||
|---|---|---|---|
| Вых. Данные | Год: 2014, Том: 6, Номер: 1, Страницы: 8-16 Страниц : 9 DOI: 10.1134/S2070050414010127 | ||
| Ключевые слова | highly dispersed catalyst, mechanical activation, molybdenum carbide, carbon | ||
| Авторы |
|
||
| Организации |
|
Реферат:
Procedures for the synthesis of massive molybdenum carbide by the mechanical activation of a mixture of MoO3, commercial carbon, and Zn in air and the synthesis of the supported carbidecontaining
catalyst Mo2C/C by the mechanical activation of commercial carbon impregnated with a 16% aqueous solution of ammonium paramolybdate in an inert atmosphere were developed for the first time. With the use of a set of physicochemical methods, the metal contents, particle sizes, specific surface areas, and phase compositions of the mechanically activated composites were determined. The structure of the carbidecontaining supported catalyst was studied by electron microscopy, and its acidic properties were studied by the temper atureprogrammed desorption of ammonia; catalytic tests in the model reactions of dibenzothiophene (DBT) and alkane aromatization were performed. It was found that the Mo2C/C catalyst exhibited high activity in these reactions: the conversion of DBT at a contact time of 3–6 h was 80–85%. The conversion of nheptane at a contact time of 2 h was 31.2%, and 100% toluene was the reaction product. An increase in the contact time to 6 h led to a decrease in the conversion of nheptane to 1.3%, and to 47% C6–C7 cycloalkanes were present in the reaction products. The results of this work are indicative of the high catalytic activity of the Mo2C/C catalyst obtained by mechanical activation.
Библиографическая ссылка:
Vasilevich A.V.
, Baklanova O.N.
, Lavrenov A.V.
, Knyazheva O.A.
, Gulyaeva T.I.
, Trenikhin M.V.
, Likholobov V.A.
Synthesis and Characterization of Massive Molybdenum Carbides and Supported CarbideContaining Catalysts Mo2C/C Prepared through Mechanical Activation
Catalysis in Industry. 2014. V.6. N1. P.8-16. DOI: 10.1134/S2070050414010127 Scopus РИНЦ OpenAlex
Synthesis and Characterization of Massive Molybdenum Carbides and Supported CarbideContaining Catalysts Mo2C/C Prepared through Mechanical Activation
Catalysis in Industry. 2014. V.6. N1. P.8-16. DOI: 10.1134/S2070050414010127 Scopus РИНЦ OpenAlex
Оригинальная:
Василевич А.В.
, Бакланова О.Н.
, Лавренов А.В.
, Княжева О.А.
, Гуляева Т.И.
, Тренихин М.В.
, Лихолобов В.А.
Синтез и исследование массивных карбидов молибдена и нанесенных карбидсодержащих катализаторов состава Mo2C/C, полученных методом механической активации
Катализ в промышленности. 2013. №6. С.21-29. РИНЦ
Синтез и исследование массивных карбидов молибдена и нанесенных карбидсодержащих катализаторов состава Mo2C/C, полученных методом механической активации
Катализ в промышленности. 2013. №6. С.21-29. РИНЦ
Даты:
| Поступила в редакцию: | 20 сент. 2013 г. |
| Опубликована в печати: | 31 дек. 2013 г. |
| Опубликована online: | 4 апр. 2014 г. |
Идентификаторы БД:
| Scopus: | 2-s2.0-84899121186 |
| РИНЦ: | 21873557 |
| OpenAlex: | W2082673998 |