MnO x -Al2O3 Catalysts for Deep Oxidation Prepared with the Use of Mechanochemical Activation: The Effect of Synthesis Conditions on the Phase Composition and Catalytic Properties Научная публикация
| Журнал |
Kinetics and Catalysis
ISSN: 0023-1584 , E-ISSN: 1608-3210 |
||||||
|---|---|---|---|---|---|---|---|
| Вых. Данные | Год: 2014, Том: 55, Номер: 5, Страницы: 639-648 Страниц : 10 DOI: 10.1134/S0023158414050048 | ||||||
| Авторы |
|
||||||
| Организации |
|
Реферат:
The catalytic activity of alumina-manganese catalysts in the oxidation of CO was studied. The MnO x -Al2O3 catalysts were prepared by an extrusion method with the introduction of mechanically activated components (manganese oxide and its mixtures with aluminum oxide, aluminum hydroxide, and a mixture of a manganese salt with aluminum hydroxide) into a paste of aluminum hydroxide followed by thermal treatment in air or argon at 1000°C. In the majority of cases, the catalysts contained a mixture of the phases of β-Mn3O4 (Mn2O3), α-Al2O3, and δ-Al2O3. The presence of low-temperature δ-Al2O3 suggested the incomplete interaction of manganese and aluminum oxides. It was found that the catalytic activity of MnO x -Al2O3 depends on the degree of interaction of the initial reactants, and its value is correlated with the amount of β-Mn3O4 in the active constituent. The intermediate thermal treatment of components at 700°C negatively affects the catalytic activity as a result of the formation of Mn2O3 and the coarsening of particles, which levels the results of mechanochemical activation. The greatest degree of interaction between Al- and Mn-containing components was reached in the selection of mechanochemical activation conditions by decreasing the size of grinding bodies, optimizing the time of mechanochemical activation, and using the mechanochemical activation of precursor mixtures. As a result of mechanochemical activation, the initial reactants were dispersed, the amounts of MnO2 and Mn2O3 changed, and defects were formed; this strengthened the interaction of components and increased catalytic activity.
Библиографическая ссылка:
Bulavchenko O.A.
, Afonasenko T.N.
, Tsyrulʹnikov P.G.
, Knyazheva O.A.
, Baklanova O.N.
, Tsybulya S.V.
MnO x -Al2O3 Catalysts for Deep Oxidation Prepared with the Use of Mechanochemical Activation: The Effect of Synthesis Conditions on the Phase Composition and Catalytic Properties
Kinetics and Catalysis. 2014. V.55. N5. P.639-648. DOI: 10.1134/S0023158414050048 WOS Scopus РИНЦ CAPlus OpenAlex
MnO x -Al2O3 Catalysts for Deep Oxidation Prepared with the Use of Mechanochemical Activation: The Effect of Synthesis Conditions on the Phase Composition and Catalytic Properties
Kinetics and Catalysis. 2014. V.55. N5. P.639-648. DOI: 10.1134/S0023158414050048 WOS Scopus РИНЦ CAPlus OpenAlex
Оригинальная:
Булавченко О.А.
, Афонасенко Т.Н.
, Цырульников П.Г.
, Княжева О.А.
, Бакланова О.Н.
, Цыбуля С.В.
MnOx Al2O3-катализаторы глубокого окисления, приготовленные с использованием механохимической активации. Влияние условий синтеза на фазовый состав и каталитические свойства
Кинетика и катализ. 2014. Т.55. №5. С.671-680. DOI: 10.7868/S0453881114050049 РИНЦ OpenAlex
MnOx Al2O3-катализаторы глубокого окисления, приготовленные с использованием механохимической активации. Влияние условий синтеза на фазовый состав и каталитические свойства
Кинетика и катализ. 2014. Т.55. №5. С.671-680. DOI: 10.7868/S0453881114050049 РИНЦ OpenAlex
Даты:
| Поступила в редакцию: | 10 июн. 2013 г. |
| Опубликована в печати: | 31 авг. 2014 г. |
| Опубликована online: | 20 сент. 2014 г. |
Идентификаторы БД:
| Web of science: | WOS:000342423300013 |
| Scopus: | 2-s2.0-84921932202 |
| РИНЦ: | 24030876 |
| Chemical Abstracts: | 2014:1579773 |
| OpenAlex: | W2039485683 |