Nanostructure analysis of the graphene layers of carbon black Научная публикация
| Конференция |
Юбилейная научная конференция "XXI век: Химия в жизнь" 24-26 апр. 2019 , Омск |
||
|---|---|---|---|
| Журнал |
AIP Conference Proceedings
ISSN: 0094-243X , E-ISSN: 1551-7616 |
||
| Вых. Данные | Год: 2019, Том: 2143, Страницы: 020010 Страниц : 4 DOI: 10.1063/1.5122909 | ||
| Авторы |
|
||
| Организации |
|
Информация о финансировании (1)
| 1 | Министерство науки и высшего образования Российской Федерации | V. 45 |
Реферат:
The information on the average distance between graphene layers, the length and curvature of layers in globules of highly dispersed carbon black was obtained. The globular turbostratic carbon material was irradiated with laser pulses. Carbon nanocapsules are formed during laser irradiation with a power density 1011 W/cm2 . The irradiation of the initial highly dispersed carbon black globules reduces the interplanar spacing of the graphene layers from 0.39 nm to 0.35 nm in the formed nanocapsules.
Библиографическая ссылка:
Trenikhin M.V.
, Drozdov V.A.
Nanostructure analysis of the graphene layers of carbon black
AIP Conference Proceedings. 2019. V.2143. P.020010. DOI: 10.1063/1.5122909 WOS Scopus РИНЦ OpenAlex
Nanostructure analysis of the graphene layers of carbon black
AIP Conference Proceedings. 2019. V.2143. P.020010. DOI: 10.1063/1.5122909 WOS Scopus РИНЦ OpenAlex
Даты:
| Опубликована online: | 16 авг. 2019 г. |
Идентификаторы БД:
| Web of science: | WOS:000505769900010 |
| Scopus: | 2-s2.0-85071244661 |
| РИНЦ: | 41658596 |
| OpenAlex: | W2968366584 |
Цитирование в БД:
Пока нет цитирований