Preparation of a Densely Packed Carbon Material

Preparation of a Densely Packed Carbon Material Full article

Journal

Solid Fuel Chemistry
ISSN: 0361-5219 , E-ISSN: 1934-8029

Output data

Year: 2019, Volume: 53, Number: 5, Pages: 303-307 Pages count : 5 DOI: 10.3103/S0361521919050033

Funding (2)

1	Ministry of Science and Higher Education of the Russian Federation	V.49.1.6
2	Ministry of Science and Higher Education of the Russian Federation	V. 45

Close-packed materials (CPMs) were prepared by pressing dispersed carbon powders with various physicochemical properties. It was found that a maximum density of CPMs based on dispersed carbon was achieved when a sample was held under pressure for 2 to 3 h, and the complete degradation of secondary structures occurred in the low-structure samples of dispersed carbon with at a pressure of no higher than 1000 MPa. The maximum density of a fullerene-based CPM was 1.67 g/cm3, and that of the dispersed carbon obtained from toluene in laboratory conditions was 1.41 g/cm3.

Dmitriev K.I.
Preparation of a Densely Packed Carbon Material
Solid Fuel Chemistry. 2019. V.53. N5. P.303-307. DOI: 10.3103/S0361521919050033 WOS Scopus РИНЦ OpenAlex

Дмитриев К.И.
Получение плотноупакованного углеродного материала
Химия твердого топлива. 2019. №5. С.53-57. DOI: 10.1134/s0023117719050037 РИНЦ OpenAlex

Submitted:	Mar 20, 2019
Accepted:	Jun 3, 2019
Published print:	Sep 1, 2019
Published online:	Oct 4, 2019

Web of science:	WOS:000488928500008
Scopus:	2-s2.0-85073194483
Elibrary:	41695804
OpenAlex:	W2978283404

Пока нет цитирований