Abstract: Mechanochemical activation was used to prepare Mg(Li)Al-layered double hydroxides (LDH) with molar ratios of cations Mg/Al = 2 and 4 and Li/Al = 0.5. The influence of cationic composition and nature of interlayer anions (CO3 2−, OH−) on the structural properties of LDH and the properties of oxide phases formed by LDH calcination was investigated by XRD and SEM. Textural properties (nitrogen adsorption–desorption isotherms at 77.4 K) and acid-base properties (CO2 double isotherm method, TPD-CO2, aldol condensation of furfural with acetone reaction) were studied in detail for mixed oxides. It was shown that mixed oxides based on the LDH that were prepared by echanochemical route have high specific surface area and porosity. An increase in the Mg/Al ratio, the introduction of Li, and the use of LDH with OH- counterions made it possible not only to increase the total basicity of mixed oxides but also to vary the fraction of basic sites with a different strength.

Cite: Stepanova L.N. , Belskaya O.B. , Vasilevich А.V. , Gulyaeva T.I. , Leont’eva N.N. , Serkova А.N. , Salanov А.N. , Likholobov V.А.
The study of structural, textural and basic properties of MgAl- and LiAl-LDH prepared by mechanochemical method
Catalysis Today. 2020. N357. P.638-645. DOI: 10.1016/j.cattod.2019.04.069 WOS Scopus РИНЦ OpenAlex

Dates:

Submitted:	Dec 24, 2018
Published print:	Apr 1, 2019
Accepted:	Apr 18, 2019

Identifiers:

Web of science:	WOS:000579549200066
Scopus:	2-s2.0-85064381940
Elibrary:	38747522
OpenAlex:	W2938590483

Citing:

DB	Citing
Scopus	24
Web of science	20
OpenAlex	33

Altmetrics: